供应高纯度PC光学数据存储OQ1023

LEXAN OQ1023 resin is an optical high purity PC resin optimized for demanding recordable and rewritable formats (CD-R, DVD-R, DVD-RW). It is also suitable for short cycletime CD and DVD production

TYPICAL PROPERTIES ⁽¹⁾
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield, 50 mm/min	60	MPa	ISO 527
Tensile Stress, break, 50 mm/min	45	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	6	%	ISO 527
Tensile Strain, break, 50 mm/min	>40	%	ISO 527
Tensile Modulus, 1 mm/min	2350	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	90	MPa	ISO 178
Flexural Modulus, 2 mm/min	2350	MPa	ISO 178
Hardness, H358/30	100	MPa	ISO 2039-1
IMPACT	Value	Unit	Standard
Izod Impact, unnotched 80103 +23°C	NB	kJ/m?	ISO 180/1U
Izod Impact, unnotched 80103 -30°C	NB	kJ/m?	ISO 180/1U
Izod Impact, notched 80103 +23°C	15	kJ/m?	ISO 180/1A
Izod Impact, notched 80103 -30°C	12	kJ/m?	ISO 180/1A
Izod Impact, unnotched 80104 +23°C	NB	kJ/m?	ISO 180/1U
Izod Impact, unnotched 80104 -30°C	NB	kJ/m?	ISO 180/1U
Izod Impact, notched 80104 +23°C	9	kJ/m?	ISO 180/1A
Izod Impact, notched 80104 -30°C	3	kJ/m?	ISO 180/1A
Charpy 23°C, V-notch Edgew 80103 sp=62mm	40	kJ/m?	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80103 sp=62mm	12	kJ/m?	ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m?	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m?	ISO 179/1eU
Charpy 23°C, V-notch Edgew 80104 sp=62mm	8	kJ/m?	ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80104 sp=62mm	NB	kJ/m?	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80104 sp=62mm	NB	kJ/m?	ISO 179/1eU
THERMAL	Value	Unit	Standard
Thermal Conductivity	0.2	W/m-°C	ISO 8302
CTE, 23°C to 80°C, flow	7.E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	7.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	138	°C	ISO 306
Vicat Softening Temp, Rate B/120	140	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm	132	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	124	°C	ISO 75/Ae
PHYSICAL	Value	Unit	Standard
Mold Shrinkage on Tensile Bar, flow (2) (5)	0.5 - 0.7	%	SABIC Method
Density	1.2	g/cm?	ISO 1183
Water Absorption, (23°C/sat)	0.35	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.15	%	ISO 62
Melt Volume Rate, MVR at 250°C/1.2 kg	8	cm?/10 min	ISO 1133
OPTICAL	Value	Unit	Standard
Light Transmission, 2.54 mm	>90	%	ASTM D 1003
Haze, 2.54 mm	<0.7	%	ASTM D 1003
Refractive Index	1.586	-	ISO 489
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	>1.E+15	Ohm-cm	IEC 60093
Surface Resistivity, ROA	>1.E+15	Ohm	IEC 60093
Dielectric Strength, in oil, 3.2 mm	17	kV/mm	IEC 60243-1
Relative Permittivity, 1 MHz	2.7	-	IEC 60250
Dissipation Factor, 1 MHz	0.01	-	IEC 60250

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	4 - 6	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	340 - 370	°C
Nozzle Temperature	340 - 370	°C
Front - Zone 3 Temperature	350 - 380	°C
Middle - Zone 2 Temperature	320 - 340	°C
Rear - Zone 1 Temperature	270 - 290	°C
Hopper Temperature	60 - 80	°C
Mold Temperature	75 - 95	°C