②原料技术数据
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
基本性能 | 熔体流动速率 | --- | ASTM D-1238 | 3.7 | g/10min |
吸水率 | 浸水24hrs后增重 | ASTM D-570 | 0.3 | % |
物理性能 | 成形收缩率 | (冷模/冷件),48hrs | ASTM D-935 | 0.2-0.6 | % |
透光率 | --- | ASTM D-1003 | 92 | % |
折射率Nd | --- | ASTM D-542 | 1.49 | --- |
比重 | --- | ASTM-D-792 | 1.19 | --- |
雾度 | --- | --- | <2 | % |
洛氏硬度 | --- | ASTM D-758(M级) | 97 | --- |
机械性能 | 拉伸强度 | --- | ASTM D-618 | 720(70) | kgf/cm2(MPa) |
弯曲强度 | --- | ASTM D-790 | 1050(103) | kgf/cm2(MPa) |
弯曲模数 | --- | ASTM D-790 | 32000 | kgf/cm2 |
冲击强度 | Izod 研磨缺口 | ASTM D256 | 1.2(12.3) | kgf-cm/cm(J/m) |
冲击强度 | 落锤(15.2×15.2×0.3cm重1.4kg半径0.64cm) | ASTM D256 | 14(1.4) | kg-cm(J) |
热 性 能 | 热变形温度负荷,退火 | 2℃/min,18.6kgf/cm2 | ASTM D-648 | 102 | ℃ |
维卡软化点 | 50℃/hr,1kg | ASTM D-1525,未退火 | 111 | ℃ |
维卡软化点 | 50℃/hr,5kg | ASTM D-1525,未退火 | 104 | ℃ |
玻璃化转变温度 | Tg | --- | 108 | ℃ |
使用温度范围 | 与残余应力大小有关 | --- | 85-102 | ℃ |
菲纳
供应PMMA塑胶原料
(1)PMMA 日本三菱IR-D50.IR-D70.IRK304.TF8.VR-L40.VRM-40 (高耐冲)MF0001.VH0001
(2)PMMA 镇江奇美CM-205、CM-207,CM-211
(3)PMMA 台湾奇美 CM-205,CM-207.CM-211
(4)PMMA 韩国LG IF850
(5)PMMA 璐彩特国际 CP-51A.CP-61A.CP-81A
(6)PMMA 法国阿科玛Vm100.V020.V040.V150
(7)PMMA 南通丽阳MF001,VH001,MD001,VH150,TF8,IRD70(耐冲击)
(8)PMMA 日本住友 LG2.HT55X.MH001
(9)PMMA 日本旭化成 560F、80N
(10)PMMA 台湾大苍T-80
(11)PMMA 德国罗姆 8N
(12)PMMA 南通三菱丽阳 MF001.VH001
长期供应PMMA塑胶原料 日本住友PMMA 镇江奇美PMMA 路彩特PMMA
备注说明: 成形方式:注塑/挤出流动性:一般特性:耐高温,耐磨性极佳。
热变形温度负荷,退火 2℃/min,18.6kgf/cm2 ASTM D-648 102 ℃
维卡软化点 50℃/hr,1kg ASTM D-1525,未退火 111 ℃
维卡软化点 50℃/hr,5kg ASTM D-1525,未退火 104 ℃
玻璃化转变温度 Tg --- 108 ℃
使用温度范围 与残余应力大小有关 --- 85-102
(东莞市PMMA V825 法国阿托厂家)