310s不锈钢化学成份 | |||
C :≤0.08, | Si :≤1.00, | Mn :≤2.00, | |
P :≤0.035, | S :≤0.030, | ||
Ni :≤19.00-22.00, | Cr :≤24.00-26.00 | ||
310s不锈钢力学性能 | |||
硬度(HB) :≤187 | 抗拉强度(бb)(Mpa) :≥520 | ||
屈服强度(σs)(Mpa) :≥205 | 伸长率(δ)% :≥40 | ||
面积缩减(ψ)% :≥50 | |||
C碳: 1.05~1.14 | Si硅: ≤0.35 | ||
Mn锰: ≤0.40 | S硫: ≤0.030 | ||
P磷: ≤0.035 | Cr铬: ≤0.25 | ||
Ni镍: ≤0.20 | Cu铜: ≤0.30 |
Steel Grade | Density(g/cm3) | ||||
钢 号 | 密 度 | ||||
304,304L,305,321 201,202,301,302 | 7.93 | ||||
316,316L,347 309S,310S | 7.98 | ||||
405,410,420 | 7.75 | ||||
409,430,434 | 7.7 | ||||
牌号 | 密度(*103千克/立方米) | 牌号 | 密度(*103千克/立方米) | ||
00Cr30Mo2 | 7.64 | 00Cr19Ni13Mo3 | 7.98 | ||
00Cr27Mo | 7.67 | 0Cr19Ni12Mo3 | 7.98 | ||
1Cr17Mo | 7.70 | 0Cr25Ni20 | 7.98 | ||
1Cr15 | 7.70 | 0Cr18Ni12Mo2Cu2 | 7.98 | ||
3Cr16 | 7.70 | 00Cr18Ni14Mo2Cu2 | 7.98 | ||
00Cr27Mo | 7.67 | 0Cr19Ni12Mo3 | 7.98 | ||
1Cr17 | 7.70 | 00Cr19Ni13Mo3 | 7.98 | ||
00Cr17 | 7.70 | 0Cr18Ni11Nb | 7.98 | ||
7Cr17 | 7.70 | 0Cr17Ni12Mo2N | 7.98 | ||
1Cr12 | 7.76 | 00Cr17Ni14Mo2 | 7.98 | ||
1Cr13 | 7.76 | 0Cr17Ni12Mo2N | 7.98 | ||
0Cr13Ai | 7.75 | 00Cr17Ni13Mo2N | 7.98 | ||
00Cr12 | 7.76 | 0Cr18Ni16Mo5 | 8.00 | ||
0Cr13Ai | 7.75 | 1Cr17Ni7 | 7.93 | ||
2Cr13 | 7.75 | 0Cr23Ni13 | 7.93 | ||
3Cr13 | 7.75 | 1Cr17Ni8 | 7.93 | ||
0Cr18Ni13Si4 | 7.75 | 1Cr18Ni9 | 7.93 | ||
00Cr18Mo2 | 7.75 | 1Cr18Ni9Si3 | 7.93 | ||
0Cr26Ni5Mo2 | 7.80 | 0Cr19Ni9 | 7.93 | ||
1Cr17Mn6Ni5N | 7.93 | 00Cr19Ni11 | 7.93 | ||
00Cr18Ni9S13 | 7.93 | 0Cr19Ni9N | 7.93 | ||
1Cr17Mn6Ni6N | 7.93 | 0Cr18Ni11Ti | 7.93 | ||
1Cr18nNi8Ni5N | 7.93 | 0Cr17Ni17Al | 7.93 |