ESTANE 58206 TPU Technical Data Sheet Type: ESTANE? 58206 is an 85A aromatic Polyester-Based Thermoplastic Polyurethane (TPU). Features: Good Flexibility at Low Temperatures and Improved Weathering Performance. Uses: Flat Die/Cast Film Extrusion and Hose/Profile Extrusion, Injection Molding. Physical Properties Value (Metric) Unit Test Method Hardness (5 sec) 85 +/- 3 Shore A ASTM D-2240 Specific Grity 1.20 ASTM D-792 Tensile Strength 7000 (48.3) psi (MPa) ASTM D-412 Ultimate Elongation 550 % “ Tensile Stress at: - 100 % Elongation 800 (5.5) psi (MPa) ASTM D-412 - 300 % Elongation 1500 (10.4) psi (MPa) “ Tear Strength Gres 500 (9.0) lb/in (kg/mm) ASTM D-624 (die C) Trouser 130 (2.3) lb/in (kg/mm) ASTM D-470 Taber Loss (1000 rev) 0.0007 (20) oz (mg) ASTM D-3389 (H18, 1000g) Tm (by DSC) 320 (160) °F (°C) Lubrizol Advanced Materials Tg (by DSC) -26 (-32) °F (°C) Lubrizol Advanced Materials ? Prior to testing samples were conditioned at 23°C for 48 hours. ? Based on extruded sheet (30 mils). ? Listed values are “typical (erage) values” and should / cannot be applied for specification pures. Supply Form and Standard Packaging ? ESTANE? 58206 TPU is supplied in pellet form and packaged in 50 lb bags or 1000 lb boxes. Material Preparation ? Prior to processing, ESTANE? 58206 TPU must be dried at 220°F (104°C) for 2-4 hours. ? It is recommended to dry the material in a desiccant type dryer. Target dew point should be -40°